Cracks were found in the exhaust ports. Most recent head showed a half inch crack in the exhaust seat. The 906 head didn't have induction hardened seats so thats probably why they don't crack. Just trying to figure out if the newer head castings (i.e 902 and 452) are prone to cracking.