100% Ar is used for aluminum work in most cases. You really don't want to use it when migging mild steel, especially thin panels, IMHO.

Ar usually creates a deep, narrow penetrating weld. Not what you need when working on sheetmetal. The C25 mix is better as it will allow you good arc quality, easier puddle control, less spatter.